Modeling the effect of unsaturated conditions on chloride penetration in one-part alkali-activated slag concrete

Sadrmomtazi, Ali; Zanganeh, Hamed

doi:10.61882/NMCE.2506.1094

Modeling the effect of unsaturated conditions on chloride penetration in one-part alkali-activated slag concrete

Document Type : Research

Authors

Ali Sadrmomtazi ¹

Hamed Zanganeh ²

¹ Professor, Department of Civil Engineering, Faculty of Engineering, University of Guilan, Rasht, Iran

² Ph.D. Candidate, Department of Civil Engineering, Faculty of Engineering, University of Guilan, Rasht, Iran.

10.61882/NMCE.2506.1094

Abstract

In this study, the effect of unsaturated conditions and curing time before exposure to an unsaturated environment on the properties of one-part alkali-activated slag concrete (O-AAS) and Ordinary Portland cement concrete (OPCC) was investigated. The samples were cured in water saturated with alkaline materials for 7, 28, 56, and 360 days. However, the specimens cured for 7, 28, and 56 days were stored in an unsaturated environment with 50% relative humidity until they reached 360 days of age. Compressive strength and rapid chloride migration tests (RCMT) were conducted at various ages up to 360 days, and corrosion initiation time was estimated by solving Fick's second law using the finite difference approach and results from RCMT. Results show that reducing the curing time before unsaturated exposure significantly decreased O-AAS's compressive strength and increased its chloride ion diffusion coefficient more significantly than OPCC. Chloride penetration modeling indicates that exposure to an unsaturated environment has a more pronounced effect on reducing the corrosion initiation time of O-AAS compared to OPCC. Also, increasing the curing time from 7 days to 56 days before exposure to an unsaturated environment caused a 186.7% increase in the estimated corrosion initiation time of O-AAS and a 20.4% increase in the estimated corrosion initiation time of OPCC. The required curing time for the O-AAS mixture to eliminate the effect of an unsaturated environment with a relative humidity of 50% on the compressive strength and chloride ion diffusion coefficient on standard specimens is 56 days, and for the OPCC mixture is 28 days.

Keywords

one-part alkali-activated slag concrete

unsaturated conditions

rapid chloride migration test

finite difference approach

corrosion initiation time

Subjects

Structural Engineering

[1] Jiang L., Niu Y., Jin W., Gao H., and Chen L., (2022). Influence of chloride salt type on chloride ion diffusion performance of alkali-activated slag mortar, Construct. Build. Mater., 351 128930, https://doi.org/10.1016/J.CONBUILDMAT.2022.128930.

[2] Duzy P., Choinska M., Hager I., Amiri O., Claverie J., (2022). Mechanical Strength and Chloride Ions’ Penetration of Alkali-Activated Concretes (AAC) with Blended Precursor. Materials, 15, 4475. https://doi.org/10.3390/ ma15134475

[3] Bagheri A., Ajam A., and Zanganeh H., (2021). Effect of very early age exposure on chloride ingress and service life performance of binary and ternary concretes. Constr. Build. Mater., 289. 123137, https://doi.org/10.1016/j.conbuildmat.2021.123137.

[4] Nasiri S., Madandoust R., Ranjbar M.M., (2023). Investigating the Calcination Temperature and Grinding Time of Calcined Clay on the Mechanical Properties and Durability of LC3 Concrete. Infrastructures, 8, 139. https://doi.org/10.3390/infrastructures8100139

[5] Ehlen, M.A. Life-365 Service Life Prediction Model and Computer Program for Predicting the Service Life and Life-Cycle Cost of Reinforced Concrete Exposed to Chlorides. 2020. User’s manual, Version 2.2.3. Produced by the Life-365™ Consortium III. http://www.life-365.org/download/Life-365_v2.2.3_Users_Manual.pdf.

[6] Nasir M., Mahmood A.H., Ashraf A. and Bahraq A.A., (2024). History, recent progress, and future challenges of alkali-activated binders – An overview, Construction and Building Materials, 426, 136141, https://doi.org/10.1016/j.conbuildmat.2024.136141

[7] Elzeadani M., Bompa D.V., and Elghazouli A.Y., (2022). One part alkali activated materials: A state-of-the-art review, Journal of Building Engineering, 57, 104871, https://doi.org/10.1016/j.jobe.2022.104871

[8] Fu Q., Bu M., Zhang Zh., Xu W., Yuan Q., and Niu D., (2023). Hydration Characteristics and Microstructure of Alkali-Activated Slag Concrete: A Review, Engineering, 20, 162–179, https://doi.org/10.1016/j.eng.2021.07.026

[9] Luukkonen T, Alkali-Activated Materials in Environmental Technology Applications, Woodhead Publishing Series in Civil and Structural Engineering, 2022.

[10] Amran M., Onaizi A.M., Makul N., Abdelgader H.S., Tang W.C., Alsulami B.T., Alluqmani A.E., and Gamil Y., (2023). Shrinkage mitigation in alkali-activated composites: A comprehensive insight into the potential applications for sustainable construction, Results in Engineering, 20, 101452, https://doi.org/10.1016/j.rineng.2023.101452

[11] Ye H., and Radlińska A., (2017). Shrinkage mitigation strategies in alkali-activated slag, Cement and Concrete Research, 101, 131–143, http://dx.doi.org/10.1016/j.cemconres.2017.08.025

[12] Wu Z., Wong H.S., and Buenfeld N.R., (2015). Influence of drying-induced microcracking and related size effects on mass transport properties of concrete, Cement and Concrete Research, 68, 35–48, http://dx.doi.org/10.1016/j.cemconres.2014.10.018

[13] Sa C.D., Benboudjema F., Thiery M., and Sicard J., (2008). Analysis of microcracking induced by differential drying shrinkage, Cement & Concrete Composites, 30, 947–956, doi:10.1016/j.cemconcomp.2008.06.015.

[14] Collins FG, and Sanjayan JG., (2000). Microcracking and strength development of alkali activated slag concrete. Cement Concrete Compos., 23(4–5), 345–352. https://doi.org/10.1016/S0958-9465(01)00003-8.

[15] Miao Y., Lu Z., Wang F., Wang H., Li Y., Lin J., and Jiang J., (2023). Shrinkage cracking evolvement in concrete cured under low relative humidity and its relationship with mechanical development, Journal of Building Engineering, 72, 106670, https://doi.org/10.1016/j.jobe.2023.106670

[16] Ogawa Y., Suzuki SH., and Kawai K., (2024). Impact of air exposure post-steam curing on the internal curing efficiency of porous ceramic roof-tile waste fine aggregate in steam-cured fly ash concrete, Materials Letters, 366, 136576, https://doi.org/10.1016/j.matlet.2024.136576

[17] Xia H., Lv X., Wang H., Song L., Zhang G., Cao D., and Chen H., (2024). Shrinkage, mechanical properties and freeze-thaw resistance of cement mortar containing internal curing materials with different absorption behaviors at low humidity, Construction and Building Materials, 416, 135182, https://doi.org/10.1016/j.conbuildmat.2024.135182

[18] Wu Z., Wong H.S., Chen C., and Buenfeld N.R., (2019). Anomalous water absorption in cement-based materials caused by drying shrinkage induced microcracks, Cement and Concrete Research, 115, 90–104, https://doi.org/10.1016/j.cemconres.2018.10.006

[19] El-Hassan H., Shehab E., and Al-Sallamin A., (2018). Influence of Different Curing Regimes on the Performance and Microstructure of Alkali-Activated Slag Concrete. Journal of Materials in Civil Engineering, 30(9), 04018230. doi:10.1061/(asce)mt.1943-5533.0002436

[20] Mohamed, O.A., (2023). Effects of the Curing Regime, Acid Exposure, Alkaline Activator Dosage, and Precursor Content on the Strength Development of Mortar with Alkali-Activated Slag and Fly Ash Binder: A Critical Review. Polymers, 15, 1248. https://doi.org/10.3390/polym15051248

[21] Prinsse S., Hordijk D.A., Ye G., Lagendijk P., and Luković M., (2020). Time-dependent material properties and reinforced beams behavior of two alkali-activated types of concrete, Struct. Concr., 21, 642-658, 10.1002/suco.201900235

[22] Wardhono A, Gunasekara C, Law DW, and Setunge S., (2017). Comparison of long term performance between alkali activated slag and fly ash geopolymer concretes. Construct Build Mater., 143, 272–279. http://dx.doi.org/10.1016/j.conbuildmat.2017.03.153

[23] Dong M., Elchalakani M., and Karrech A., (2020). Development of high strength one-part geopolymer mortar using sodium metasilicate, Construction and Building Materials, 236, 117611, https://doi.org/10.1016/j.conbuildmat.2019.117611

[24] ASTM C150, Standard specification for Portland Cement, ASTM International, Philadelphia, PA, 2017.

[25] ASTM C989, Standard specification for Slag cement for use in concrete and mortars, ASTM International, Philadelphia, PA, 2017.

[26] ASTM C33, Standard specification for concrete aggregates, ASTM International, Philadelphia, PA, 2017.

[27] Marvila M.T., Garcez de Azevedo A.R., Linhares Junior J.A.T., and Vieira C.M.F., (2023). Activated alkali cement based on blast furnace slag: effect of curing type and concentration of Na20, Journal of Materials Research and Technology, 23, 4551–4565, https://doi.org/10.1016/j.jmrt.2023.02.088

[28] ASTM C157, Standard test method for length change of hardened cement mortar and concrete, ASTM International, Philadelphia, PA, 2017.

[29] ASTM C39, standard test method for compressive strength of cylindrical concrete specimens, ASTM International, Philadelphia, PA, 2017.

[30] NT Build 492, Chloride migration coefficient from Non-steady sate migration experiments, NORDTEST, Finland, 1999.

[31] Rahmani K., Nasrollahzadeh K., and Rostami M., (2023). Experimental Study on the Effects of Aggregate Content and Fibers on Mechanical Properties of One-Part Alkali-Activat-ed Slag Concrete, Journal of Concrete Structures and Materials, 8 (2), 146-162.

[32] Bagheri A., Ajam A., and Zanganeh H., (2019). Investigation of chloride ingress into concrete under very early age exposure conditions, Constr. Build. Mater., 225, 801–811, https://doi.org/10.1016/j.conbuildmat.2019.07.225.

[33] Yu X., Li J., Yu Y., and Song A., (2024). Advancing service life estimation of reinforced concrete considering the coupling effects of multiple factors: Hybridized physical testing and machine learning approach, Journal of Building Engineering, 84, 108476, https://doi.org/10.1016/j.jobe.2024.108476